| Prod Model: |
Dia1-6inch |
| Markets: |
North America,South America,Eastern Europe,Southeast Asia,Africa |
| Size: |
Dia. 20-150mm |
| Raw Material: |
65mn,B2,#45 |
| Hardness: |
55-65HRC |
| Impact Value: |
Higher Than 12j/Cm2 |
| Drop Times: |
Higher Than 20,000.00 |
| Breakage Rate: |
Lower Than 1% |
| Heat Treatment: |
Water-Quenching & Tempering |
| Surface Treatment: |
Polished Finished |
| Quality Promise: |
SGS |
| Certificate: |
ISO9001:2008 |
| Material: |
Chrome Alloyed Steel |
| Processing Type: |
Casting |
Product Description
Ag mill steel forging ball
Professional manufacturer of steel forging ball and grinding media cylpebs.
Details of H&G Ag mill steel forging ball
1. Size: Dia. 20mm-150mm
2. Material: B2,B6,65MN,#45
3. Characteristics: high hardness, good wear resistant, low breakage, no deformation.
4. Hardness: 55-65HRC; Breakage rate ≤1%; Drop times≥10,000.00
5. Application: mining, cement, metallurgy, power plants, chemical and magnets industries.
6. Function: grinding media.
7. Packing style
Container Bags: Dia20mm-Dia150mm, 1000Kgs/Container Nylon Ton Bag (GW:1001Kgs)
Steel Drums: Dia20mm-Dia80mm, 900Kgs/Drum (GW: 915Kgs)
Dia90mm-Dia150mm 850Kgs/Drum (GW: 865Kg)
Why choosing H&G forged ball ?
1. Over 20 years Professional casting grinding ball manufacturing experience, deserves your trust.
2. High quality, competitive price and good service benefit our customers. ISO9001 certified company, advanced oil quenching and heating production line, together with advanced testing machines imported from Germany are used to ensure the quality.
3. Skilled sales & service team in Shanghai branch can provide timely good service.
4. 20,000 Tons annual production capacity can provide short L/T.
Details of Our Factory
H&G Wear-resistant Material Co., Ltd. is one of the largest manufacturers for steel forging ball, liners for balls mill and grinding cylpebs in China. We are ISO9001 certified company with the annual production capacity over 20,000 metric tons.
ISO9001:2008
|
Chemical Elements |
|
Material |
Chemical Elements (%) |
|
C |
Mn |
Si |
Cr |
S |
P |
|
50MN |
0.48-0.56 |
0.70-1.0 |
0.17-0.37 |
≤0.25 |
≤0.035 |
≤0.035 |
|
60MN |
0.57-0.65 |
0.50-0.80 |
0.17-0.37 |
≤0.25 |
≤0.035 |
≤0.035 |
|
65MN |
0.62-0.70 |
0.90-1.20 |
0.17-0.37 |
≤0.25 |
≤0.035 |
≤0.035 |
|
75Mn |
0.72-0.92 |
0.70-1.20 |
0.17-0.37 |
0.4-0.6 |
≤0.035 |
≤0.035 |
|
75MnCr |
0.70-0.85 |
0.70-0.80 |
0.17-0.37 |
0.2-0.7 |
≤0.03 |
≤0.03 |
|
75SiMn |
0.70-0.90 |
0.70-1.20 |
0.4-0.8 |
≤0.25 |
≤0.03 |
≤0.03 |
|
B2 |
0.70-0.85 |
0.70-0.80 |
0.17-0.37 |
0.2-0.7 |
≤0.035 |
≤0.035 |
|
40Cr |
0.37-0.44 |
0.50-0.80 |
0.17-0.37 |
0.8-1.10 |
≤0.035 |
≤0.035 |
|
45# |
0.42-0.50 |
0.50-0.80 |
0.17-0.37 |
≤0.25 |
≤0.035 |
≤0.035 |
|
Physical Property & Microstructure |
|
Material |
AK.J/cm2 |
Falling Ball Times |
Surface HRC |
Core HRC |
Microstructure |
|
50MN |
≥12 |
≥10000 |
≥56 |
≥48 |
M+C |
|
60MN |
≥15 |
≥12000 |
≥58 |
≥50 |
M+C |
|
65MN |
≥15 |
≥12000 |
≥60 |
≥50 |
M+C |
|
75Mn |
≥17 |
≥12000 |
≥60 |
≥52 |
M+C |
|
75MnCr |
≥16 |
≥12000 |
≥60 |
≥50 |
M+C |
|
75SiMn |
≥17 |
≥12000 |
≥60 |
≥54 |
M+C |
|
B2 |
≥15 |
≥12000 |
≥60 |
≥50 |
M+C |
|
45# |
≥12 |
≥10000 |
≥52 |
≥45 |
M+C |
|
Martensite Carbide |
Xuzhou H&G Wear-resistant Material Co., Ltd. was established in 1989, located in Xuzhou, Jiangsu Province. Through more than 20 years' striving, we have become one of the leading enterprises in the same industry. Our company is devoted to researching, developing, producing and selling grinding balls, grinding cylpebs, and ball mill liner plates, which are widely used in cement, mining and chemical industries, and power plants, etc...Our manufacturing base covers 30 mu, with the standard workshop area of 12, 000 sqm. Three advanced casting manufacturing lines, and sophisticated testing equipment guarantee a stable and resistant product quality. Our annual productivity is 20, 000 tons.
Company History
In 1989, Liubang Casting Factory, as a individual, was established. We mainly used coke smelting reduction technics, and the products were casting grinding balls and bars.
In 1996, Peixian County Tongda Casting Co., Ltd. was established. We became a general taxpayer. One medium frequency furnace production line was introduced into our production, together with the annealing process technics.
In 2002, our factory was moved to Liubang Industrial Park, Peixian County, Jiangsu Province. The overall property had a qualitative improvement
In 2008, renamed as Xuzhou H&G Wear Resistant Co., Ltd...12, 000 square meters standard workshop, 3 medium frequency furnace production lines, 2 furnace annealing equipment, and 2 oil-immersed heat treatment equipment were put into production. Also, better technology and equipment was used for IQC and OQC.
In 2012, D-win Metal Material (Shanghai) Co., Ltd. was established in Shanghai, a wholly owned sales subsidiary, intending to develop international business.
In 2013, 800 square meters office building was put into use in our factory, making great progress in both work environment and employees.